Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX973 - Europe - (PPE+PA*) - Saudi Basic Industries Corporation (SABIC)

Check here, which other Noryl GTX datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 기타 특성 - Processing Recommendation Injection Molding - 도표

Any use of this information falls under the rules of our disclaimer.

제품 설명서

NORYL GTX™ 973 resin is a conductive, non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized to allow for in- or on-line primer-less electrostatic and powder coat painting. NORYL GTX973 resin exhibits high impact resistance and strength and is an excellent candidate for automotive painted applications such as body panels, fenders, and tank flaps.

UL Yellow Card Link E45329-269624

Processing/Physical Characteristics	값	단위	시험규격
ISO 데이터
용융 부피 - 흐름 속도, MVR	12	cm³/10min	ISO 1133
온도	280	°C	-
하중	5	kg	-
용융 밀도	945	kg/m³	-
용융 열전도율	0.22	W/(m K)	-
용융 비열용량	2610	J/(kg K)	-
이형온도	240	°C	-
ASTM 데이터
용융 흐름성, MFI	20	g/10min	ASTM D 1238
온도	280	°C	-
하중	5	kg	-

기계적 특성	값	단위	시험규격
ISO 데이터
인장탄성률	2300	MPa	ISO 527
항복강도	60	MPa	ISO 527
항복변형률	4	%	ISO 527
파단시 강도	55	MPa	ISO 527
파단시 신율	30	%	ISO 527
굴곡 계수	2300	MPa	ISO 178
챠피 노치드 충격 강도, +23°C	15	kJ/m²	ISO 179/1eA
챠피 노치드 충격 강도, -30°C	6	kJ/m²	ISO 179/1eA
아이조드 노치 충격 강도, +23°C, 4mm	15	kJ/m²	ISO 180/1A
아이조드 노치 충격 강도, -30°C, 4mm	7	kJ/m²	ISO 180/1A
ASTM 데이터
인장탄성률	2200	MPa	ASTM D 638
항복강도	60	MPa	ASTM D 638
파단시 강도	55	MPa	ASTM D 638
항복변형률	5	%	ASTM D 638
파단시 신율	55	%	ASTM D 638
굴곡 계수	2300	MPa	ASTM D 790
아이조드 충격은 노치, 1/8 in	130	J/m	ASTM D 256
아이조드 충격은 노치, Low-Temperature	80	J/m	ASTM D 256
온도	-30	°C	-

열적 특성	값	단위	시험규격
ISO 데이터
비카트 연화 온도, B	195	°C	ISO 306
비카트 연화 온도, 120°C/h 50N	200	°C	ISO 306
선형 열팽창 계수, 평행	90	E-6/K	ISO 11359-1/-2
선형 열팽창 계수, 수직	90	E-6/K	ISO 11359-1/-2
1.5mm 평균두께에서의 난연성	HB	class	IEC 60695-11-10
테스트 두께	1.5	mm	-
Glow Wire Flammability Index (GWFI)	675	°C	IEC 60695-2-12
Glow Wire Flammability Index (GWFI)	675	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (GWIT)	675	°C	IEC 60695-2-13
GWIT - thickness tested (2)	2	mm	-
Glow Wire Ignition Temperature (GWIT)	675	°C	IEC 60695-2-13
GWIT - thickness tested (3)	3	mm	-
ASTM 데이터
DTUL @ 66 psi	195	°C	ASTM D 648
비카트 연화 온도	200	°C	ASTM D 1525

기타 특성	값	단위	시험규격
물에서의 흡수성	4.2	%	ISO 62와 유사
조건에서의 흡습성	1.2	%	ISO 62와 유사
밀도	1100	kg/m³	ISO 1183
밀도	1090	kg/m³	ASTM D 792

Processing Recommendation Injection Molding	값	단위	시험규격
Pre-drying - Temperature	100 - 120	°C	-
Pre-drying - Time	2 - 3	h	-
Processing humidity	≤0.07	%	-
용융수지온도	290 - 320	°C	-
성형온도	100 - 120	°C	-
Feed temperature	60 - 80	°C	-
Zone 1	260 - 280	°C	-
Zone 2	280 - 300	°C	-
Zone 3	290 - 320	°C	-

도표

특징

생산 공정

사출 성형

응용

자동차의

지역별 검색

짱쨌쨈

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com